Pacific Northwest National Laboratory researchers have upended what’s known about how rechargeable batteries function.

Rechargeable battery performance could be improved by a new understanding of how they work at the molecular level. For decades, researchers have assumed that the inevitable filmy buildup on electrodes inside rechargeable batteries is the driver of performance loss. Research shows that view is backward.

The research report has been published in Nature Energy.

The buildup of mossy or tree-like structured lithium metal deposits on battery electrodes is not the root cause of performance loss, but rather a side effect. The report shows the first direct measurement of the electrical properties at the boundary between the solid electrode and the liquid electrolyte inside a rechargeable battery.

In-situ transmission electron microscopy allows researchers to observe directly how the materials in a battery evolve at atomic scale, providing insight into rechargeable battery function. Image Credit: Andrea Starr | Pacific Northwest National Laboratory. Click the press release link for more larger and more images.

The study, led by a research team at the Department of Energy’s Pacific Northwest National Laboratory, shows that the so-called solid electrolyte interphase (SEI) is not an electronic insulator, as previously thought, but instead behaves like a semiconductor. The research solves the long-standing mystery of how SEI functions electrically during battery operation.

Chongmin Wang, a PNNL Laboratory Fellow and battery technology expert who co-led the study said, “A higher rate of electrical conductance induces a thicker SEI with intricate solid lithium forms, ultimately leading to inferior battery performance.”

Micro-sized battery upends assumptions about how rechargeable batteries work

The researchers focused on this SEI layer, which is thinner than a sheet of tissue paper, because of its out-sized role in battery performance. This filmy mosaic selectively permits charged lithium ions to cross during discharge and controls movement of electrons that supply the battery’s power.

When batteries are new, the SEI forms on the first charging cycle and ideally remains stable during the battery’s expected lifespan. But a look inside an aging rechargeable battery often reveals substantial buildup of solid lithium on the negative electrodes. Battery researchers have assumed that this buildup causes the performance losses. Part of the reason for this guess work has been an inability to make measurements to test cause and effect.

Wang, along with co-lead of the study Wu Xu, a materials scientist of PNNL’s Battery Materials and Systems Group, co-first authors Yaobin Xu and Hao Jia, and their colleagues at PNNL, Texas A&M University, and Lawrence Berkeley National Laboratory solved this problem by developing a new technique to directly measure electrical conduction across the SEI in an experimental system. The team combined transmission electron microscopy with nanoscale manipulation of microfabricated metal needles inside the microscope. The researchers then measured the electrical properties of the SEI layer formed on either a copper or lithium metal with four different types of electrolytes.

The group’s measurements revealed that as voltage increases in the battery, the SEI layer in all cases leaks electrons, making it semi-conductive.

Findings suggest carbon-containing molecules leak electrons, reducing battery life

 Once they had recorded this semiconductor-like behavior, which had never been directly observed previously, they wanted to understand which components of the chemically complex SEI are responsible for the electron leakage.

“We found that the carbon-containing organic components of the SEI layer are prone to leaking electrons,” Xu said.

The researchers concluded that minimizing the organic components in SEI would enable the batteries to have longer useful life.

“Even slight variations of the rate of conduction through the SEI can result in dramatic differences in efficiency and battery cycling stability,” Wang added.

***

It will take a while for the lessons this research offers to saturate the battery industry and there will be some time involved for battery designers to research and adapt electrolytes to optimize the battery performance and lifetime.

But better batteries are coming. When cycle lifetimes are extended and capacity looses are minimized our products will have more value and give better longer service lives.