Argonne National Laboratory researchers have uncovered a new avenue for overcoming the performance decline that occurs with repeated cycling in the cathodes of sodium ion batteries. This discovery could find applications in batteries for transportation and the electric grid.

Battery-powered vehicles have made a significant dent in the transportation market. But that market still needs lower cost batteries that can power vehicles for greater ranges. Also desirable are low-cost batteries able to store for the grid the intermittent clean energy from solar and wind technologies and power hundreds of thousands of homes.

To meet those needs, researchers around the world are racing to develop batteries beyond the current standard of lithium-ion designs. One of the more promising candidates is the sodium-ion battery. It is particularly attractive because of the greater abundance and lower cost of sodium compared with lithium. What’s more, when cycled at high voltage (4.5 volts), a sodium-ion battery can greatly increase the amount of energy that can be stored in a given weight or volume. However, its fairly rapid performance decline with charge-discharge cycling has stymied commercialization.

Cross-section SEM image of the strained O3 NaNi0.4Mn0.4Co0.2O2. Image Credit: Argonne National Laboratory. Click image for the largest view.

Researchers at the U.S. Department of Energy’s (DOE) Argonne National Laboratory have discovered a key reason for the performance degradation: the occurrence of defects in the atomic structure that form during the steps involved in preparing the cathode material. These defects eventually lead to a structural earthquake in the cathode, resulting in catastrophic performance decline during battery cycling. Armed with this knowledge, battery developers will now be able to adjust synthesis conditions to fabricate far superior sodium-ion cathodes.

The team published their research in Nature Communications in an article entitled, “Native lattice strain induced structural earthquake in sodium layered oxide cathodes.”

Key to making this discovery was the team’s reliance on the world-class scientific capabilities available at Argonne’s Center for Nanoscale Materials (CNM) and Advanced Photon Source (APS), both of which are DOE Office of Science user facilities.

Guiliang Xu, assistant chemist in Argonne’s Chemical Sciences and Engineering division said, “These capabilities allowed us to track changes in the atomic structure of the cathode material in real time while it is being synthesized.”

During cathode synthesis, material fabricators slowly heat the cathode mixture to a very high temperature in air, hold it there for a set amount of time, then rapidly drop the temperature to room temperature.

Yuzi Liu, a CNM nanoscientist said, “Seeing is believing. With Argonne’s world-class scientific facilities, we do not have to guess what is happening during the synthesis.” To that end, the team called upon the transmission electron microscope in CNM and synchrotron X-ray beams at the APS (at beamlines 11-ID-C and 20-BM).

Their data revealed that, upon rapidly dropping the temperature during material synthesis, the cathode particle surface had become less smooth and exhibited large areas indicating strain. The data also showed that a push-pull effect in these areas happens during cathode cycling, causing cracking of the cathode particles and performance decline.

Upon further study, the team found that this degradation intensified when cycling cathodes at high temperature (130° Fahrenheit) or with fast charging (one hour instead of 10 hours).

Khalil Amine, an Argonne Distinguished Fellow noted, “Our insights are extremely important for the large-scale manufacturing of improved sodium-ion cathodes. Because of the large amount of material involved, say, 1000 kilograms, there will be a large temperature variation, which will lead to many defects forming unless appropriate steps are taken.”

Earlier research by team members had resulted in a greatly improved anode. “Now, we should be able to match our improved cathode with the anode to attain a 20% – 40% increase in performance,” said Xu. “Also important, such batteries will maintain that performance with long-term cycling at high voltage.”

The impact could result in a longer driving range in more affordable electric vehicles and lower cost for energy storage on the electric grid.

In addition to Xu, Liu and Amine, authors include Xiang Liu, Xinwei Zhou, Chen Zhao, Inhui Hwang, Amine Daali, Zhenzhen Yang, Yang Ren, Cheng-Jun Sun and Zonghai Chen. Zhou and Liu performed the analyses at CNM while Ren and Sun did the analyses at APS.

***

This news is sure to trigger some process engineering innovation., Sodium does offer enough of a leap in potential to knock lithium ion off the market top. But lets not get into expectations just yet. There are other issues to work out and lithium ion has a couple of decades of refinements already done. Getting to market isn’t going to be easy.